Plicast Si-Bond M AL

Product: Plicast Si-Bond M AL

Product #: 14779

Service Temperature Limit
Aluminum Contact – 2000oF

Non-Contact – 2800°F

Installation Method: Casting

Shelf Life: 4 months

Industries: Aluminum

Best Applications

Primary lining material or aluminum furnace repair, contact applications include:

  1. Furnace lower walls and belly bands
  2. Furnace upper walls where splash or dross growth occurs
  3. Ramps, sills, jambs and dry hearths
  4. Ladles

Product Information

Plibrico’s Plicast® Si-Bond M Al is a mullite based, cementless castable enhanced for resistance to aluminum reaction and flux attack.  This material contains a minimal amount of lime and other alkalis making its matrix highly resistant to high temperature fluxing.  In aluminum contact and non-contact applications it provides the following benefits:

  • Excellent resistance to aluminum attack and corundum growth even at elevated temperatures
  • High, consistent hot strength from the aluminum melt range to high temperature >2300oF
  • Enhanced mineralogy and low porosity for improved flux and alkali resistance
  • Quicker bake out than reduced cement castable options

Available Internationally As: Plico® Castable Si-Bond M Al

/by

Pli-Shot Si-Bond M AL

Service Temperature Limit

Aluminum Contact – 2000oF

Non-Contact – 2800°F

Installation Method

Shotcrete

Shelf Life

4 months

Industries

Aluminum

Best Applications

Primary lining material or aluminum furnace repair, contact applications include:

  1. Furnace lower walls and belly bands
  2. Furnace upper walls where splash or dross growth occurs
  3. Ramps, sills, jambs and dry hearths
  4. Ladles

Product Information

Pli-shot Si-Bond M Al is a mullite based, cementless castable enhanced for resistance to aluminum reaction and flux attack.   It is a version of Plicast® Si-Bond M Al that has been modified for shotcrete application.   This product offers improved pumping characteristics and a longer stiffening time.  In aluminum contact and non-contact applications it provides the following benefits:

  • Excellent resistance to aluminum attack and corundum growth even at elevated temperatures
  • High, consistent hot strength from the aluminum melt range to high temperature >2300oF
  • Enhanced mineralogy and low porosity for improved flux and alkali resistance
  • Quicker bake out than reduced cement castable options
/by

Pli-Shot Si-Bond M

Product: Pli-Shot Si-Bond M

Product #: 15417

Service Temperature Limit:  3100°F

Installation Method:  Shotcreting

Shelf Life:  4 months

Industries:  Steel/Non-ferrous, Mineral Processing, Medical Waste, Power Generation, Boilers, Incineration, Thermal Oxidizers

Best Applications:  Engineered to be used as a primary lining material in a wide array of industrial furnace and kiln applications, including:

  1. Reheat and forge furnace walls and roofs
  2. Medical waste furnace walls & roofs
  3. Incinerators & Thermal Oxidizer linings
  4. Mineral Processing Kilns

Plibrico TDS Link – https://plibri.co/2Ssdgm4

Product Information: Pli-Shot™ Si-Bond™ M is a mullite-based, no cement, shotcrete material.   Developed with optimized chemistry and mineralogy, this material was engineered for enhanced performance at elevated temperatures above 2000°F.   Superior hot strength performance above 2000°F, this product performs great in highly corrosive environments and also works well in a wide range of applications.   Material must be used in conjunction with Plibrico’s sodium silicate activator.   Product advantages include:

  • Superior hot strengths at 2000°F and above compared to low and ultra-low cement refractory materials
  • Good abrasion resistance
  • Low porosity
  • Good thermal shock resistance
  • Great resistance to alkali and slag attack
  • Less sensitive to colder weather installations
  • Good pumping characteristics

Available Internationally As:  Plico Shotecrete Si-Bond M

Plibrico SDS Link – https://plibri.co/3wvYI3j

/by

Pli-Shot Si-Bond B

Product: Pli-Shot Si-Bond B

Product #: 3178

Service Temperature Limit: 3100°F

Installation Method:  Shotcreting

Shelf Life:  4 months

Industries:  Mineral Processing, Aluminum, Steel, Waste-to-Energy, Boilers, Incineration, Sulfur Recovery

Best Applications:  Engineered for higher temperature industrial applications, including:

  1. Cement Kiln preheaters
  2. Mineral Processing Kilns – alumina and aggregate calcining
  3. Steel/Ferrous – reheat/forge furnace hearths, jambs, lintels and sill
  4. Boilers – coal and oil fired
  5. Incinerators and Thermal Oxidizers – combustion and quench chambers
  6. Sulfur Recovery Units
  7. Aluminum – furnace upper walls and roofs

Plibrico TDS Link – https://plibri.co/3HAmgel

Product Information: Pli-Shot™ Si-Bond™ B is a high alumina cement free castable, formulated into a shotcrete application.   Based on a bauxite aggregate, this material contains a minimal amount of lime and other alkalis, rendering it’s matrix very resistant to high temperature fluxing.   In addition, Pli-Shot Si-Bond B is more resistant to slags (acidic through neutral) and alkali attacks than a low or ultra-low cement castables of a similar chemistry.   Other product characteristics and benefits include:

  • High hot strength 1500°F to 2500°F, and above
  • High alumina mineralogy and low porosity for improved slag resistance
  • Resistant to alkali vapor attack
  • Good refractoriness under load
  • Very good abrasion resistance: 9cc per ASTM C704
  • Good volume stability
  • Quicker bake out than reduced cement castable options

Available Internationally As:  Plico® Shotcrete Si-Bond B

Plibrico SDS Link – https://plibri.co/39BDWcS

/by

Plicast Si-Bond SP

Service Temperature Limit

3100°F

Installation Method

Casting

Shelf Life

4 Months

Industries

Pulp & Paper, Waste-To-Energy, Incineration, Aluminum, Off Gas

Best Applications

As a primary lining material in high alkali environments (slag or gas) or in contact with moderately basic slags.  Applications include:

  1. Black liquor boilers
  2. Cement kiln preheaters
  3. Incinerators and thermal oxidizers
  4. Biomass furnaces – slag zones

Product Information

Plicast® Si-Bond SP is a high alumina based, cement less castable, modified with a magnesium aluminate spinel addition.   This castable was specifically developed for enhanced resistance to high alkali slags and alkali vapor attacks.   In lab alkali slag cup tests versus more traditional high alumina cement bonded castable both with and without spinel additions, Plicast Si-Bond SP consistently:

  • Retained slag
  • Resisted alkali bursting – all cement bonded castables routinely burst due alkali absorption

These results were confirmed by independent testing at Missouri S&T (Rolla) in a DOE funded project for black liquor gasifiers.

Plicast Si-Bond SP out performed all other commercial castables tested in this project.   As a result, there have been very successful commercial applications in black liquor boilers.   In addition to its outstanding alkali resistance, Plicast Si-Bond SP also exhibits exceptional hot strength up through 2500°F.

/by

Plicast Si-Bond M

Product: Plicast Si-Bond M

Product #: 14781

Service Temperature Limit: 3100°F

Installation Method: Casting or Pumping

Shelf Life: 4 months

Industries: Aluminum, Mineral Processing, Steel, Boilers, Incineration, Off-Gas

Best Applications: Great for use in higher temperature industrial applications and precast shapes including:

  1. Precast Shapes – including burner cones and piers – various industries
  2. Mineral Processing Kilns – alumina and aggregate calcining
  3. Steel/Ferrous – reheat/forge furnace hearths, jambs, lintels and sill
  4. Boilers – coal and oil fired
  5. Ladles
  6. Incinerators and Thermal Oxidizers – combustion and quench chambers
  7. Sulfur Recovery Units
  8. Aluminum – furnace upper walls and roofs

Plibrico TDS Link – https://plibri.co/2yjBYLM

Product Information: Plicast® Si-Bond M is a mullite based, cementless castable. Since it contains a minimal amount of lime and other alkalis, it’s matrix is resistant to high temperature fluxing. Plicast Si-Bond M also offers better resistance to slags that are acidic to neutral, as well as alkali attacks than a low or even ultra-low cement castables of a similar chemistry. Other product characteristics and benefits include:

  • Excellent resistance to aluminum attack and corundum growth even at elevated temperatures
  • High hot strength above 1500°F to 2500°F and above
  • Enhanced mineralogy and low porosity for improved slag alkali resistance
  • Good refractoriness under load
  • Very good abrasion resistance
  • Good volume stability
  • Moderate thermal conductivity
  • Quicker bake out than reduced cement castable options
  • Plicast Si-Bond M has good flow and setting characteristics allowing it to be place by vibration, casting or pumping.

Available Internationally As: Plico® Castable Si-Bond M

Plibrico SDS Link – https://plibri.co/2ysCozd

/by

Plicast Si-Bond B

Product: Plicast Si-Bond B

Product #: 14778

Service Temperature Limit: 3200°F

Installation Method:  Casting or Pumping

Shelf Life:  4 months

Industries:  Mineral Processing, Aluminum, Steel, Waste-to-Energy, Boilers, Incineration, Sulfur Recovery

Best Applications:  Engineered for higher temperature industrial applications and precast shapes including:

  1. Precast Shapes – including burner cones and piers – various industries
  2. Cement Kiln preheaters
  3. Mineral Processing Kilns – alumina and aggregate calcining
  4. Steel/Ferrous – reheat/forge furnace hearths, jambs, lintels and sill
  5. Boilers – coal and oil fired
  6. Ladles
  7. Incinerators and Thermal Oxidizers – combustion and quench chambers
  8. Sulfur Recovery Units
  9. Aluminum – furnace upper walls and roofs

Plibrico TDS Link – https://plibri.co/3kLEr4g

Product Information: Plicast® Si-Bond™ B is a high alumina cementless castable.   Based on a bauxite aggregate, this material contains a minimal amount of lime and other alkalis, rendering it’s matrix very resistant to high temperature fluxing.   In addition, Plicast Si-Bond B is more resistant to slags (acidic through neutral) and alkali attacks than a low or ultra-low cement castables of a similar chemistry.   Other product characteristics and benefits include:

  • High hot strength 1500°F to 2500°F, and above
  • High alumina mineralogy and low porosity for improved slag resistance
  • Resistant to alkali vapor attack
  • Good refractoriness under load
  • Very good abrasion resistance: 9cc per ASTM C704
  • Good volume stability
  • Quicker bake out than reduced cement castable options

Plicast Si-Bond B has good flow and setting characteristics allowing it to be place by vibration, casting or pumping.

Available Internationally As:  Plico® Castable Si-Bond B

Plibrico SDS Link – https://plibri.co/2ysCozd

/by

This site uses cookies. By continuing to browse the site, you are agreeing to our use of cookies.

AcceptLearn more

  • Plibrico® Plastic Refractories

    Clay/Air Bond

    Product Name %Al2O3 Service Limit SDS
    Plibrico®Super F AB 58% 2900F / 1590C SDS
    Plibrico®60 AB 58% 3100F / 1705C SDS
    Plibrico®80 AB 78% 3200F / 1760C SDS
    Plibrico®90 AB 90% 3400F / 1871C SDS

    Phosphate Bond

    Product Name %Al2O3 Service Limit SDS
    Plibrico®55 S 54% 3000F / 1648C SDS
    Plibrico®68 S 68% 3100F / 1705C SDS
    Plibrico®68 SA 68% 3100F / 1705C SDS
    Plibrico®85 S Special 83% 3300F / 1815C SDS
    Plibrico®90 S 90% 3400F / 1870C SDS
    Plibrico®SiC 80 (80% SiC) 2700F / 1480C SDS

    (fine grain – soft)

    Product Name %Al2O3 Service Limit SDS
    Plibrico®SR 68 68% 3100F / 1705C SDS
    Plibrico®SR 85 83% 3300F / 1815C SDS
    Plibrico®SR 90 88% 3400F / 1870C SDS

    Plibrico HyRATE® Plastic Refractories – Gunning Grade

    Clay/Air Bond

    Product Name %Al2O3 Service Limit SDS
    Plibrico HyRATE®Super F AB 43% 2900F / 1595C SDS
    Plibrico HyRATE®60 AB 60% 3100F / 1705C SDS
    Plibrico HyRATE®80 AB 78% 3200F / 1760C SDS

    Phosphate Bond

    Product Name %Al2O3 Service Limit SDS
    Plibrico HyRATE®68 S 68% 3100F / 1705C SDS
    Plibrico HyRATE®85 S Special 84% 3300F / 1815C SDS